Abstract
This specification covers stainless steel wire and welded wire reinforcements from hot-rolled stainless steel rod to be used as concrete reinforcement with corrosion resistant and magnetic permeability properties. The material shall be cold-worked, drawn or rolled, and plain or deformed. Materials shall adhere to deformation requirements. Tensile, yield, and weld shear strengths shall be measured. Bend tests shall also be performed. Dimensional requirements and permissible variations in width, length, weight, density, cross-sectional area, diameter, and average spacings of wires are specified. Guidelines for sampling, inspection, rejection, retest, certification, and packaging are given.
Scope
1.1 This specification covers stainless steel wire and welded wire reinforcement produced from hot-rolled stainless steel rod. The stainless steel wire is cold-worked, drawn or rolled, plain (non-deformed) or deformed or a combination of deformed and plain. It is used as concrete reinforcement for applications requiring resistance to corrosion or controlled magnetic permeability, or both. Common wire sizes and dimensions are found in this specification. Actual wire sizes are not restricted to those shown in the tables.
1.2 Supplement S1 describes high strength wire, which shall be furnished when specifically ordered. It shall be permissible to furnish high strength wire in place of regular wire if mutually agreed to by the purchaser and supplier.
1.3 The chemical composition of the steel (stainless grade) shall be selected for suitability to the application involved by agreement between the manufacturer and the purchaser. Use Specification A276 for chemical requirements. The UNS designations are to be included with the type number and noted in brackets, i.e. austenitic stainless steels as Type 304 [S30400], 304L [S30403], 316 [S31600], 316L [S31603], 316N [S31651], 316LN [S31653] and duplex stainless steels, Types 2205 [S32205] and 329 [S32900].
1.4 Wire for welded wire reinforcement is generally manufactured at 520 MPa [75 ksi] yield strength level. Other strength levels shall be by agreement between the purchaser and manufacturer.
1.5 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.