Significance and Use
The THE test method is designed to provide highly reproducible crevice repassivation potentials for corrosion–resistant alloys (for example, Alloy 22) in a wide range of environments from non-aggressive to highly aggressive. In conditions of low environmental aggressiveness (such as low temperature or low chloride concentration), corrosion–resistant alloys such as Alloy 22 will resist crevice corrosion initiation and the cyclic potentiodynamic polarization test (Test Method G 61
The more noble this crevice corrosion repassivation potential (ER,CREV) value, the more resistant the alloy is to crevice corrosion in the tested electrolyte. This is similar to other test methods to measure localized corrosion resistance such as Test Method G 61
This test method may be used to rank several alloys by using the same testing electrolyte and temperature. It can also be used to determine the response of a given alloy when the environmental conditions (such as electrolyte composition and temperature) change.
Scope
1.1 This test method covers a procedure for conducting anodic polarization studies to determine the crevice repassivation potential for corrosion–resistant alloys. The concept of the repassivation potential is similar to that of the protection potential given in Reference Test Method G 5.
1.2 The test method consists in applying successively potentiodynamic, galvanostatic, and potentiostatic treatments for the initial formation and afterward repassivation of crevice corrosion.
1.3 This test method is a complement to Test Method G 61
1.4 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.