BS EN ISO 18592:2009 Resistance welding. Destructive testing of welds. Method for the fatigue testing of multispot- welded specimens
BS EN ISO 18592 is an International Standard which specifies test specimens and procedures for performing constant load amplitude fatigue tests on multi-spot-welded and multi-axial specimens. It applies where the thickness of the specimen ranges from 0,5 mm to 5 mm at room temperature and a relative humidity of max. 80 %.
The applicability of BS EN ISO 18592 to larger thicknesses can be limited by mechanical properties such as yield strength and formability of the specimen material. The thickness range for advanced high strength steels (AHSS) is generally below 3,0 mm. Greater thicknesses apply for aluminium alloys, for example.
Contents of BS EN ISO 18592:
Foreword
Introduction
1 Scope
2 Normative references
3 Terms and definitions
4 Symbols and abbreviated terms
5 Specimens
5.1 General
5.2 Selection of suitable specimens
5.3 Specimen fabrication
5.4 Specimen geometry
6 Requirements for testing machine
7 Specimen grips and alignment
7.1 General
7.2 Shear and peel loading
8 Test procedure
8.1 General
8.2 Mounting the H-specimens
8.3 Clamping procedure for the H-specimens
8.4 Fatigue test
8.5 Test termination
9 Test report
9.1 Basic information
9.2 Presentation of fatigue test results
Annex A (informative) Calibration specimen for verifying the load distribution in H-specimens
Annex B (informative) Hydraulic grips for the fatigue testing of H-specimens
Annex C (informative) Grip for the fatigue testing of H-specimens
Annex D (informative) Flow chart — Data acquisition
Bibliography